(01-02-2016, 11:42 PM)Highpower Wrote: According to my highly calibrated Japanese hardness testing files I'm estimating about 53 - 54 HRC after the tempering.
Maybe a tad towards the high side, but I'd say that was just about right. It's not seeing a lot of impact/shock type force, so it should hold up quite well.
Full of ideas, but slow to produce parts